Lithium molybdenum purple bronze

{{Short description|Chemical compound}}

Lithium molybdenum purple bronze is a chemical compound with formula {{chem|Li|0.9|Mo|6|O|17}}, that is, a mixed oxide of molybdenum and lithium. It can be obtained as flat crystals with a purple-red color and metallic sheen (hence the "purple bronze" name).

This compound is one of several molybdenum bronzes with general formula {{chem|A|x|Mo|y|O|z}} where A is an alkali metal or thallium Tl. It stands out among them (and also among the sub-class of "purple" molybdenum bronzes) for its peculiar electrical properties, including a marked anisotropy that makes it a "quasi-1D" conductor, and a metal-to-insulator transition as it is cooled below 30 K.

Preparation

The compound was first obtained by Martha Greenblatt and others by a temperature gradient flux technique. In a typical preparation, a stoichometric melt of {{chem|Li|2|MoO|4}}, {{chem|MoO|2}} and {{chem|MoO|3}} is maintained in a temperature gradient from 490 to 640 °C oven 15 cm in vacuum over several days. Excess reagents are dissolved with a hot potassium carbonate solution releasing metallic-purple plate-like crystals, a couple mm wide and less than a mm thick.

Structure

The crystal structure of {{chem|Li|0.9|Mo|6|O|17}} was determined by Onoda and others through single-crystal X-ray diffraction. The crystal system is monoclinic, with approximate unit cell dimensions a = 1.2762 nm, b = 0.5523 nm, and c = 0.9499 nm, with angle β = 90.61°, volume V = 0.6695 nm3 and Z = 2. In typical crystals, a is the shortest dimension (perpendicular to the plates) and b the longest. The density is 4.24 g/cm3. The structure is rather different from that of potassium molybdenum purple bronze {{chem|K|0.9|Mo|6|O|17}}, except that both are organized in layers. The difference may be explained by the relative sizes of the {{chem|K|+}} and {{chem|Li|+}} ions.

The unit cell contains six crystallographically independent molybdenum sites. One-third of the molybdenum atoms are surrounded by four oxygens, two thirds are surrounded by six oxygens. The crystal is a stack of slabs; each slab consists of three layers of distorted {{chem|MoO|6}} octahedra sharing corners. The lithium ions are inserted in the large vacant sites between the slabs. There are zigzag chains of alternating molybdenum and oxygen atoms extending along the b axis.

Properties

Lithium molybdenum purple bronze is quite different than the sodium, potassium and thallium analogs. It has a three-dimensional crystal structure, but a pseudo-one-dimensional (1D) metallic character, eventually becoming a superconductor at about 2 K. Its properties are most spectacular below 5 meV. The Tomonaga-Luttinger liquid theory has been invoked to explain its anomalous behavior.

= Electrical conductivity=

At room temperature, Greenblatt and others (in 1984) measured the resistivity of lithium purple bronze along the a, b and c axes as 2.47 Ω cm, 0.0095 Ω cm, and on the order of 0.25 Ω cm, respectively. The conductivities would be in the ratio 1:250:10, which would make this compound an almost one-dimensional conductor. However, Da Luz and others (2007) measured 0.079, 0.018, and 0.050 Ω cm, respectively, which corresponds to conductivity ratios 1:6:2.4 for a:b:c; whereas H. Chen and others (2010) measured 0.854, 0.016, and 0.0645 Ω cm, respectively, which correspond to conductivity ratios of 1:53:13.

This anisotropy has been attributed to the crystal structure, specifically to the zig-zag chains of molybdenum and oxygen atoms

= Resistivity and temperature =

The resistivity along all three axes increases linearly with temperature from about 30 K to 300 K, as in a metal. This is anomalous since such a law is expected above the Debye temperature (= 400 K for this compound) The resistivity ratios along the three axes are preserved in that range.

= Metal-insulator transition =

As the lithium purple bronze is cooled from 30 K to 20, it changes abruptly to an insulator. After reaching a minimum at about 24 K, the resistivity increases 10-fold and becomes somewhat more isotropic, with conductivities 1:25:14. The anisotropy is partially restored if a magnetic field is applied perpendicular to the b axis. The transition may be related to the onset of a charge density wave. Santos and others have observed that the thermal expansion coefficient is largest along the a axis, so cooling will bring the conducting chains closer together, leading to a dimensional cross-over. The theory of Luttinger liquids then predicts such behavior. Anyway, as of 2010 there was no consensus explanation for this transition. In 2023 it has been suggested that the strange behaviour could be by emergent symmetry (in contrast to symmetry breaking) from interference between the conduction electrons and dark excitons{{Cite journal |last=Chudzinski |first=P. |last2=Berben |first2=M. |last3=Xu |first3=Xiaofeng |last4=Wakeham |first4=N. |last5=Bernáth |first5=B. |last6=Duffy |first6=C. |last7=Hinlopen |first7=R. D. H. |last8=Hsu |first8=Yu-Te |last9=Wiedmann |first9=S. |last10=Tinnemans |first10=P. |last11=Jin |first11=Rongying|author11-link=Rongying Jin |last12=Greenblatt |first12=M. |last13=Hussey |first13=N. E. |date=2023-11-17 |title=Emergent symmetry in a low-dimensional superconductor on the edge of Mottness |url=https://www.science.org/doi/10.1126/science.abp8948 |journal=Science |language=en |volume=382 |issue=6672 |pages=792–796 |doi=10.1126/science.abp8948 |issn=0036-8075}}{{Cite web |last=Tomé |first=César |date=2023-11-21 |title=Purple bronze, from insulator to superconductor and back |url=https://mappingignorance.org/2023/11/21/instant-transition-from-insulator-to-superconductor-and-back/ |access-date=2023-12-02 |website=Mapping Ignorance |language=en-US}}

= Superconducting state =

Lithium molybdenum purple bronze becomes superconductor between 1 and 2 K.

=Thermal conductivity=

Li0.9Mo6O17, due to spin–charge separation, can have a much higher thermal conductivity than predicted by the Wiedemann-Franz law.

[https://www.sciencedaily.com/releases/2011/07/110720103517.htm Wiedemann-Franz Law: Physicists break 150-year-old empirical laws of physics],[https://www.nature.com/articles/ncomms1406 Gross violation of the Wiedemann–Franz law in a quasi-one-dimensional conductor Wakeham et al. 2011]

= Magnetoresistance =

The magnetoresistance of lithium purple bronze is negative when the magnetic field is applied along the b-axis, but large and positive when the field is applied along the a-axis and the c-axis.

See also

References

{{cite journal | last1=Greenblatt | first1=M. | last2=McCarroll | first2=W.H. | last3=Neifeld | first3=R. | last4=Croft | first4=M. | last5=Waszczak | first5=J.V. | title=Quasi two-dimensional electronic properties of the lithium molybdenum bronze, Li0.9Mo6O17 | journal=Solid State Communications | publisher=Elsevier BV | volume=51 | issue=9 | year=1984 | issn=0038-1098 | doi=10.1016/0038-1098(84)90944-x | pages=671–674| bibcode=1984SSCom..51..671G }}

{{cite journal | last1=Whangbo | first1=Myung Hwan. | last2=Canadell | first2=Enric. | title=Band electronic structure of the lithium molybdenum purple bronze Li0.9Mo6O17 | journal=Journal of the American Chemical Society | publisher=American Chemical Society (ACS) | volume=110 | issue=2 | year=1988 | issn=0002-7863 | doi=10.1021/ja00210a006 | pages=358–363}}

Martha Greenblatt (1996), "Molybdenum and tungsten bronzes: Low-dimensional metals with unusual properties". In C. Schlenker ed., "Physics and Chemistry of Low-Dimensional Inorganic Conductors" Book, Springer, 481 pages. {{ISBN|9780306453045}}

{{cite journal | last1=Boujida | first1=Mohamed | last2=Escribe-Filippini | first2=Claude | last3=Marcus | first3=Jacques | last4=Schlenker | first4=Claire | title=Superconducting properties of the low dimensional lithium molybdenum purple bronze Li0.9Mo6O17 | journal=Physica C: Superconductivity | publisher=Elsevier BV | volume=153-155 | year=1988 | issn=0921-4534 | doi=10.1016/0921-4534(88)90685-5 | pages=465–466| bibcode=1988PhyC..153..465B }}

{{cite journal | last1=dos Santos | first1=C. A. M. | last2=White | first2=B. D. | last3=Yu | first3=Yi-Kuo | last4=Neumeier | first4=J. J. | last5=Souza | first5=J. A. | title=Dimensional Crossover in the Purple Bronze Li0.9Mo6O17 | journal=Physical Review Letters | publisher=American Physical Society (APS) | volume=98 | issue=26 | date=2007-06-28 | issn=0031-9007 | doi=10.1103/physrevlett.98.266405 | page=266405| pmid=17678113 | bibcode=2007PhRvL..98z6405D }}

{{cite journal | last1=Chudzinski | first1=P. | last2=Jarlborg | first2=T. | last3=Giamarchi | first3=T. | title=Luttinger-liquid theory of purple bronze Li0.9Mo6O17 in the charge regime | journal=Physical Review B | volume=86 | issue=7 | date=2012-08-27 | issn=1098-0121 | doi=10.1103/physrevb.86.075147 | page=075147| arxiv=1205.0239 | bibcode=2012PhRvB..86g5147C | s2cid=53396531 | url=https://archive-ouverte.unige.ch/unige:35553 }}

{{cite journal | last1=Onoda | first1=M. | last2=Toriumi | first2=K. | last3=Matsuda | first3=Y. | last4=Sato | first4=M. | title=Crystal structure of lithium molybdenum purple bronze Li0.9Mo6O17 | journal=Journal of Solid State Chemistry | publisher=Elsevier BV | volume=66 | issue=1 | year=1987 | issn=0022-4596 | doi=10.1016/0022-4596(87)90231-3 | pages=163–170| bibcode=1987JSSCh..66..163O }}

{{cite journal | last1=Chen | first1=H. | last2=Ying | first2=J. J. | last3=Xie | first3=Y. L. | last4=Wu | first4=G. | last5=Wu | first5=T. | last6=Chen | first6=X. H. | title=Magnetotransport properties in purple bronze Li0.9Mo6O17 single crystal | journal=EPL (Europhysics Letters) | publisher=IOP Publishing | volume=89 | issue=6 | date=2010-03-01 | issn=0295-5075 | doi=10.1209/0295-5075/89/67010 | page=67010| arxiv=0906.3855 | bibcode=2010EL.....8967010C | s2cid=122903841 }}

{{cite journal | last1=da Luz | first1=M. S. | last2=dos Santos | first2=C. A. M. | last3=Moreno | first3=J. | last4=White | first4=B. D. | last5=Neumeier | first5=J. J. | title=Anisotropic electrical resistivity of quasi-one-dimensional Li0.9Mo6O17 determined by the Montgomery method | journal=Physical Review B | publisher=American Physical Society (APS) | volume=76 | issue=23 | date=2007-12-21 | issn=1098-0121 | doi=10.1103/physrevb.76.233105 | page=233105| bibcode=2007PhRvB..76w3105D }}

{{Lithium compounds}}

Category:Molybdenum compounds

Category:Lithium compounds

Category:Oxides